Double-sided Heat-sealable Film
After the product is simply printed, it is used for hexahedron and pillow packaging.
Category:
Product Introduction
Product Features
- Excellent oxygen and oil barrier performance
- Excellent heat seal strength
- Good smooth and open
Typical Thickness
15,18,23,25,27,32,37,46,50μm. Special specifications can be customized according to customer requirements.
Technical Data
| NO. | Properties | Direction | Unit | Testing Methods | Standard |
| 1 | Tensile strength | MD TD | MPa | ASTM-D882 GB/T 1040.3-2006 | ≥120 |
| ≥230 | |||||
| 2 | Elongation at break | MD TD | % | ASTM-D882 GB/T 1040.3-2006 | ≤180 |
| ≤65 | |||||
| 3 | Shrinkage 120°C×5min | MD TD | % | ASTM-D1204 GB/T 10003-2008 | ≤4.0 |
| ≤2.5 | |||||
| 4 | Kinetic coefficient of friction | IN/IN OUT/OUT | / | ASTM-D1894 GB 10006-1988 | ≤0.30 |
| ≤0.30 | |||||
| 5 | Surface tension | IN OUT | Mn/m | ASTM-D2578 GB/T 14216-2008 | ≥38 |
| / | |||||
| 6 | Haze | / | % | ASTM-D1003 GB 2410-2008 | ≤3.0 |
| 7 | Gloss（45℃） | / | % | ASTM-D1003 GB 8807-1988 | ≥90 |
| 8 | Heat seal strength at 115℃-130℃ , 1 bar, 1 sec | IN/IN OUT/OUT | N/15mm | GB/T10003-2008 | ≥2.5 |
| ≥2.5 | |||||
| 9 | Heat sealing temperature 1 bar, 1 sec | / | ℃ | ASTM F88/F88M GB/T 10003-2008 | / |
| 10 | Surface resistance | IN/IN | Ω | GB/T 1410-2008 | ≤n*1012 |
The values given in the above table are typical performance data for reference only.
If you have special requirements for product performance indexes, please communicate with business manager.
Keywords:
Keywords:
Double-sided Heat-sealable Film
Contact Us
Tel:+86 18506085685
Address: No.166 Fuju Road, Yinxi Street, Fuqing City, Fuzhou City, Fujian Province, China
WeChat Official Account